Uamea efuefu o uʻamea ia e faʻaititia i mea lelei ninii ma o ni mea muamua ia e faʻaaoga mo le tele o 3D lolomiina gaioiga e maua ai vaega uʻamea. O le lolomiga 3D, e taʻua foi ole faʻaopopoga gaosi (AM), o le gaosiaina o vaega ma oloa i totonu ole laiga. Uma uiga o le uʻamea pauta ma le ituaiga o le 3D lolomiina gaioiga fuafua ai meatotino o le iʻuga oloa. O le faʻamalamalamaina o le efuefu e faʻamoemoeina i le auala na gaosia ai, lea e ono iʻu ai i le eseesega o vaega ma faʻamamāina.


Oloa Faʻamatalaga

Pine o oloa

Uamea stainless, Ituaiga ; 316L
Uiga Faʻaletino lapoʻa tele 15-53 μm
Foliga Lalolagi
tafe 40 S (mita tafe Hall)
manino foliga 3.9 g / cm3
Density 7.98 g / cm3
Vaega o vailaʻau Fe Nofoaga
Cr 16 ~ 18 wt%
Ni 10 ~ 14 wt%
Mo 2 ~ 3 wt%
Mn ≤2 wt%
Si ≤1 wt%
C ≤0.05 wt%
P ≤0.045 wt%
S ≤0.03 wt%
O ≤0.1 wt%
Vaega o meatotino Uiga tele Approx. 99,9%
Malosi malosi Approx.560 MPa
Galue malosi Approx.480 MPa
Elongation pe a uma le gau Approx .20%
Elasticity modulus Approx.180 GPa
Faigata Approx.85 HRB (158 HB)
Uʻamea filogia alumini , Ituaiga: AlSi10Mg
Uiga Faʻaletino lapoʻa tele 15-53 μm
Foliga Lalolagi
tafe 150 S (mita tafe Hall)
manino foliga 1.45 g / cm3
Density 2.67 g / cm3
Vaega o vailaʻau Al Nofoaga
Si 9 ~ 10 wt%
Mg 0.2 ~ 0.45 wt%
Cu ≤0.05 wt%
Mn ≤0.45 wt%
Ni ≤0.05 wt%
Fe ≤0.55 wt%
Ti ≤0.15 wt%
C ≤0.0075wt%
Vaega o meatotino Uiga tele ≥95%
Malosi malosi Approx. 330 MPa
Galue malosi Approx. 245 MPa
Elongation pe a uma le gau Approx. 6%
Elasticity modulus Approx. 70 GPa
Faigata Approx. 120 HB

 

 Uʻamea filogia Titanium, Ituaiga: TC4 (Ti-6Al-4V)
Uiga Faʻaletino lapoʻa tele 15-45 μm
Foliga Lalolagi
tafe 45 S (mita tafe Hall)
manino foliga 2.5 g / cm3
Density 4.51 g / cm3
Vaega o vailaʻau Ti Nofoaga
Al 5 ~ 6.75 wt%
V 3.5 ~ 4.5 wt%
Fe ≤0.25 wt%
C ≤0.02 wt%
Y ≤0.005 wt%
O 0.14 ~ 0.16 wt%
N ≤0.02 wt%
Cu ≤0.1 wt%
Isi 0.4 wt%
Vaega o meatotino Uiga tele Approx .99.9%
Malosi malosi Approx.1000 MPa
Galue malosi Approx.900 MPa
Elongation pe a uma le gau Approx. 10%
Elasticity modulus Approx.110 GPa
Faigata Approx.300 HV (294 HB)

 

Nickel-base superalloy Ituaiga: IN718
Uiga Faʻaletino lapoʻa tele 15-53 μm
Foliga Lalolagi
tafe 40 S (mita tafe Hall)
manino foliga 4.1 g / cm3
Density 8.15 g / cm3
Vaega o vailaʻau Ni 50 ~ 55 wt%
Cr 17 ~ 22 wt%
Nb 4.75 ~ 5.5 wt%
Mo 2.8 ~ 3.3 wt%
Co ≤1 wt%
C ≤0.08 wt%
P ≤0.015 wt%
Si ≤0.35 wt%
Al 0.2 ~ 0.8 wt%
Ti 0.65 ~ 1.15 wt%
Fe Nofoaga
Vaega o meatotino Uiga tele ≥99%
Malosi malosi Approx. 980 MPa (1240 MPa pe a maeʻa togafitiga vevela)
Galue malosi Approx. 780 MPa (1000 MPa pe a maeʻa togafitiga vevela)
Elongation pe a uma le gau 12 ~ 30%
Elasticity modulus Approx. 160 GPa
Faigata Approx. 30 HRC (47 HRC pe a maeʻa togafitiga vevela)

 

Uamea faʻamamaina sila: Ituaiga: MS1
Uiga Faʻaletino lapoʻa tele 15-53 μm
Foliga Lalolagi
tafe 40 S (mita tafe Hall)
manino foliga 4.3 g / cm3
Density 8 g / cm3
Vaega o vailaʻau Fe Nofoaga
Co 8.5 ~ 9.5 wt%
Ni 17 ~ 19 wt%
Mo 4.2 ~ 5.2 wt%
Mn ≤0.1 wt%
Ti 0.6 ~ 0.8 wt%
C ≤0.03 wt%
Al 0.05 ~ 0.15 wt%
S ≤0.01 wt%
Cr ≤0.3 wt%
Vaega o meatotino Uiga tele ≥99%
Malosi malosi Arrpox.1090 MPa (1930 MPa pe a maeʻa togafitiga vevela)
Galue malosi Arrpox.1000 MPa (1890 MPa pe a maeʻa togafitiga vevela)
Elongation pe a uma le gau Arrpox.4%
Elasticity modulus Arrpox.160 GPa (180 GPa pe a maeʻa togafitiga vevela)
Faigata Arrpox.35 HRC
 Uʻamea filogia Cobalt-chromium , Ituaiga: MP1 (CoCr-2Lc)
Uiga Faʻaletino lapoʻa tele 15-53 μm
Foliga Lalolagi
tafe 40 S (mita tafe Hall)
manino foliga 4.1 g / cm3
Density 8.3 g / cm3
Vaega o vailaʻau Co Nofoaga
Cr 26 ~ 30 wt%
Mo 5 ~ 7 wt%
Si ≤1 wt%
Mn ≤1 wt%
Fe ≤0.75 wt%
C ≤0.16 wt%
Ni ≤0.1 wt%
Vaega o meatotino Uiga tele ≥99%
Malosi malosi Approx.1100 MPa
Galue malosi Approx.900 MPa
Elongation pe a uma le gau Approx. 10%
Elasticity modulus Approx.200 GPa
Faigata 35 ~ 45 HRC (323 ~ 428 HB)

 